Wafer-bonding structure and method of forming thereof

ABSTRACT

A method of forming a wafer-bonding structure includes a wafer-bonding step, a through silicon via (TSV) forming step, and a forming bonding pad step. In the wafer-bonding step, at least two wafers are corresponding to and bonded to each other by bonding surfaces thereof. In the TSV forming step, a TSV structure is formed on at least one side of a seal ring structure of one of the wafers, a conductive filler is disposed in the TSV structure, and the TSV structure is overlapped the side of one of the seal ring structure of one of the wafers and a portion of a seal ring structure of another one of the wafers. In the forming bonding pad step, a bonding pad is formed on an outer surface which is relative to the bonding surface of the wafer with the TSV structure, so as to form the wafer-bonding structure.

BACKGROUND Technical Field

The present disclosure relates to a wafer-bonding structure and a methodof forming thereof.

Description of Related Art

Nowadays, a wafer-bonding structure is well established technology for awafer-level packaging. In a significant effort is focused on awafer-level three-dimensional integration as a viable solution forincreasing functionality and overcoming a bottleneck of a wire-bondingprocess.

However, an oxide is easily formed on a bonding surface of a wafer toincrease a resistance of the wafer-bonding structure. Also, an edgechipping and a moisture penetration are easily happened during sawingthe wafer-bonding structure. Hence, decreasing an effect of the oxideformed on the bonding surface and avoiding the edge chipping and themoisture penetration as possible are important for the wafer-bondingstructure.

SUMMARY

According to one aspect of the present disclosure, a method of forming awafer-bonding structure includes a wafer-bonding step, a through siliconvia (TSV) forming step, and a forming bonding pad step. In thewafer-bonding step, at least two wafers are corresponding to and bondedto each other by bonding surfaces thereof. In the TSV forming step, aTSV structure is formed on at least one side of a seal ring structure ofone of the wafers, a conductive filler is disposed in the TSV structure,and the TSV structure is overlapped the side of the seal ring structureof one of the wafers and a portion of a seal ring structure of anotherwafer. In the forming bonding pad step, a bonding pad is formed on anouter surface which is relative to the bonding surface of the wafer withthe TSV structure, so as to form the wafer-bonding structure.

According to another aspect of the present disclosure, a wafer-bondingstructure includes at least two wafers, a through silicon via (TSV)structure, a conductive filler and a bonding pad. The wafers are bondedto each other, each of the wafers has a bonding surface, and each of thewafers includes a seal ring structure. The seal ring structure isdisposed in the wafer, an end of the seal ring structure is connected tothe bonding surface, and the other end of the seal ring structure isconnected to an outer surface of the wafer. The TSV structure is passedthrough from the outer surface to the bonding surface in one of thewafers, wherein the TSV structure is connected to and overlapped atleast one side of the seal ring structure of one of the wafers and aportion of the seal ring structure of another one of the wafers. Theconductive filler is disposed in the TSV structure. The bonding pad isdisposed on the outer surface of the wafer with the TSV structure.

BRIEF DESCRIPTION OF THE DRAWINGS

The present disclosure can be more fully understood by reading thefollowing detailed description of the embodiment, with reference made tothe accompanying drawings as follows:

FIG. 1 is a step flow chart of a method of forming a wafer-bondingstructure according to an embodiment of the present disclosure.

FIG. 2 is a schematic view of the surface treatment step according tothe embodiment of FIG. 1.

FIG. 3 is a schematic view of the wafer-bonding step according to theembodiment of FIG. 1.

FIG. 4 is a schematic view of the through silicon via step according tothe embodiment of FIG. 1.

FIG. 5 is a schematic view of the forming bonding pad step according tothe embodiment of FIG. 1.

DETAILED DESCRIPTION

FIG. 1 is a step flow chart of a method of forming a wafer-bondingstructure 100 according to an embodiment of the present disclosure. InFIG. 1, the method of forming the wafer-bonding structure 100 includes asurface treatment step S101, a wafer-bonding step S102, a throughsilicon via (TSV) forming step S103 and a forming bonding pad step S104.

FIG. 2 is a schematic view of the surface treatment step S101 accordingto the embodiment of FIG. 1. In FIGS. 1 and 2, a bonding surface of eachof at least two wafers is performed a surface treatment before thewafer-bonding step S102. According to the embodiment of FIG. 1, a numberof the wafers is two, but is not limited thereto. Further, the wafer 21has the bonding surface 21 a, and the wafer 22 has the bonding surface22 a. In detail, the surface treatment step S101 is to densify a siliconoxide (not shown) on the bonding surfaces 21 a, 22 a to avoid voidsformed by the bonding surfaces 21 a, 22 a. Also, a roughness of thebonding surfaces 21 a, 22 a is less than 1.5 nm.

FIG. 3 is a schematic view of the wafer-bonding step S102 according tothe embodiment of FIG. 1. In FIGS. 1 and 3, each of the wafers 21, 22are corresponding to and bonded to each other on the bonding surfaces 21a, 22 a thereof. Each of the wafers has a seal ring structure. Indetail, according to the embodiment of FIG. 1, the wafer 21 has a sealring structure 210, the wafer 22 has a seal ring structure 220, and theseal ring structures 210, 220 are aligned to each other. Furthermore, analignment accuracy of the wafer-bonding step S102 can be below 300 nm,but is not limited thereto. In detail, the alignment accuracy could beconfirmed via a wafer testing structure.

Moreover, the wafer 21 includes the seal ring structure 210, and thewafer 22 includes the seal ring structure 220. Each of the seal ringstructure 210 is corresponding to each of the seal ring structures 220.Furthermore, in the wafer-bonding step S102, the wafers 21, 22 areexposed to a nitrogen plasma or an oxygen plasma, and the wafers 21, 22are bonded at 250° C. to 350° C. for 1 hour to 3 hours. Therefore, it isfavorable for promoting a connecting strength between the wafers 21, 22.

FIG. 4 is a schematic view of the TSV forming step S103 according to theembodiment of FIG. 1. In FIGS. 1 and 4, a TSV structure 230 is formed onat least one side of a seal ring structure of one of the wafers 21, 22after a formation of an oxide layer 260, a conductive filler 240 isdisposed in the TSV structure 230, and the TSV structure 230 isoverlapped the side of the seal ring structure of the wafer 21.According to the embodiment of FIG. 1, the TSV structure 230 is formedon two sides of the seal ring structure 210 of the wafer 21, and the TSVstructure 230 is overlapped the sides of the seal ring structure 210 ofthe wafer 21, but is not limited thereto. It should be mentioned thatthe TSV structure 230 overlapped the sides of the seal ring structure210 of the wafer 21 is favorable for enhancing a mechanical protectionand a humidity protection of the wafer-bonding structure 200.

Moreover, the TSV structure 230 is overlapped a portion of the seal ringstructure 220 of the wafer 22. In detail, the TSV structure 230 isformed from an outer surface (its reference numeral is omitted) to thebonding surface 21 a of the wafer 21. Therefore, the TSV structure 230with the conductive filler 240 is favorable for improving a connectingstrength between the wafers 21, 22. Also, an electrical resistancebetween the wafers 21, 22 can be decreased via the TSV structure 230with the conductive filler 240.

In detail, the conductive filler 240 is disposed in the TSV structure230 via a sputtering and plating process, and a chemical-mechanicalpolishing (CMP) is performed on the outer surface of the wafer 21 toavoid the outer surface of the wafer 21 being not uneven.

FIG. 5 is a schematic view of the forming bonding pad step S104according to the embodiment of FIG. 1. In FIGS. 1 and 5, a bonding pad250 is formed on the outer surface which is relative to the bondingsurface 21 a of the wafer with the TSV structure 230, so as to form thewafer-bonding structure 200. According to the embodiment of FIG. 1, thebonding pad 250 is formed on the outer surface of the wafer 21 after theformation of an oxide layer 260 over the wafer-bonding structure 200,and the bonding pad 250 is for a wire-bonding process.

Via the method of forming the wafer-bonding structure, the connectingstrength between the wafers can be stronger. Moreover, the resistantbetween the wafers can be decreased.

In FIG. 5, the wafer-bonding structure 200 of the present disclosureincludes the wafers 21, 22, the TSV structure 230, the conductive filler240, the bonding pad 250 and the oxide layer 260.

In detail, the wafers 21, 22 are bonded, the wafer 21 has the bondingsurface 21 a, and the wafer 22 has the bonding surface 22 a. The wafer21 includes the seal ring structure 210 disposed in the wafer 21, an endof the seal ring structure 210 is connected to the bonding surface 21 a,and the other end of the seal ring structure 210 is connected to theouter surface of the wafer 21. The wafer 22 includes the seal ringstructure 220 disposed in the wafer 22, a side of the seal ringstructure 210 is connected to the bonding surface 22 a, and the otherside of the seal ring structure 220 is connected to an outer surface(its reference numeral is omitted) of the wafer 22.

The TSV structure 230 is passed through from the outer surface to thebonding surface in one of the at least two wafers, wherein the TSVstructure 230 is connected to and overlapped at least one side of theseal ring structure of one of the wafers and a portion of the seal ringstructure of another wafer. According to the embodiment of FIG. 5, theTSV structure 230 is passed through from the outer surface to thebonding surface 21 a in the wafer 21, wherein the TSV structure 230 isconnected to and overlapped the sides of the seal ring structure 210 ofthe wafer 21 and the portion of the seal ring structure 220 of wafer 22.In detail, the TSV structure 230 is connected to and overlapped aportion of the first metal layer 221, but is not limited thereto.Therefore, it is favorable for increasing the conductivity between thewafers 21, 22. The conductive filler 240 is disposed in the TSVstructure 230. The bonding pad 250 is disposed on the outer surface ofthe wafer 21 with the TSV structure 230. The conductive filler 240 canbe made of copper, but is not limited thereto.

In detail, the oxide layer 260 is disposed on the outer surface of thewafer 21 with the TSV structure 230, and the bonding pad 250 is disposedon the oxide layer 260. Further, the oxide layer 260 can be made of asilicon oxide, but is not limited thereto.

Furthermore, each of the seal ring structures can include a first metallayer, at least one metal layer and at least two pin sets. In detail,according to the embodiment of FIG. 5, the seal ring structure 210includes the first metal layer 211, the metal layers 212, 213, 214 andthe pin sets 215; the seal ring structure 220 includes the first metallayer 221, the metal layers 222, 223, 224 and the pin sets 225. Thefirst metal layer 211 is connected to the bonding surface 21 a, and thefirst metal layer 221 is connected to the bonding surface 22 a. Themetal layers 212, 213, 214 are disposed between the outer surface andthe first metal layer 211, and the metal layers 222, 223, 224 aredisposed between the outer surface and the first metal layer 221. One ofthe pin sets 215 is connected to the first metal layer 211 and the metallayer 214, another one of the pin sets 215 is connected to the metallayers 213, 214, another one of the pin sets 215 is connected to themetal layers 212, 213, and another one of the pin sets 215 is connectedto the metal layer 212 and the outer surface. One of the pin sets 225 isconnected to the first metal layer 221 and the metal layer 224, anotherone of the pin sets 225 is connected to the metal layers 223, 224,another one of the pin sets 225 is connected to the metal layers 222,223, and another one of the pin sets 225 is connected to the metal layer222 and the outer surface. According to the embodiment of FIG. 5, anumber of the pin sets 215 is four, a number of the pin sets 225 isfour, and the numbers of the pin sets 215, 225 are corresponding to thenumber of the metal layers 212, 213, 214, 222, 223, 224. Further, anumber of the metal layer is not limited thereto. The first metal layers211, 221 and the metal layers 212, 213, 214, 222, 223, 224 can be madeof copper. The bonding pad 250 can be made of aluminum.

Furthermore, each of the pin sets 215, 225 includes at least three pins.A width of each of the pins 215, 225 can be larger than or equal to0.025 μm, and a number of the pins is larger than or equal to three, butis not limited thereto. Therefore, it is favorable for avoiding an edgechipping and a moisture penetration during a sawing process.

Moreover, a width of the first metal layer 211 is larger than widths ofthe metal layers 212, 213, 214, and a width of the first metal layer 221is larger than widths of the metal layers 222, 223, 224. In detail, thewidth of the metal layer 214 is larger than the width of the metal layer213, and the width of the metal layer 213 is larger than the metal layer212; the width of the metal layer 224 is larger than the width of themetal layer 223, and the width of the metal layer 223 is larger than themetal layer 222. Therefore, it is favorable for increasing aconductivity between the first metal layer and the metal layers.

In FIGS. 2 to 5, the width of the first metal layer 221 is larger thanthe width of the first metal layer 211. Therefore, the TSV structure 230can go through to reach the wafer 22, and the TSV structure 230 can bestraddled the portion of the first metal layer 221.

Further, a range of the TSV structure 230 straddled the first metallayer 211 can be larger than or equal to 0.05 μm, and a range of the TSVstructure 230 straddled each of the metal layers 212, 213, 214 can belarger than or equal to 0.02 μm. In detail, the range of the TSVstructure 230 straddled the metal layer 212 is larger than or equal to0.02 μm, the range of the TSV structure 230 straddled the metal layer213 is larger than or equal to 0.03 μm, and the range of the TSVstructure 230 straddled the metal layer 214 is larger than or equal to0.04 μm, but is not limited thereto. Therefore, it is favorable forincreasing the conductivity between the wafers 21, 22.

Furthermore, a depth of the TSV structure 230 can be 2 μm to 20 μm, anda width of the TSV structure 230 can be 0.1 μm to 10 μm. Further, adepth of the TSV structure 230 can be 4 μm to 7 μm, but is not limitedthereto. It is worth mentioning that the depth of the TSV structure 230is corresponding to a thickness of the wafer 21, and the width of theTSV structure 230 is corresponding to the range of the TSV structure 230straddled the first metal layer 211 and the metal layers 212, 213, 214.

In detail, the seal ring structures 210, 220 are corresponding to aground electric potential (Vss) of the wafer-bonding structure 200.Also, every power supply electric potential (VCC) (not shown) of thewafers 21, 22 could be connected in parallel. A voltage from every VCCof the wafers 21, 22 is passed through a lowest resistance. Furthermore,an additional electrical connection for the seal ring structures 210,220 is provided via the TSV structure 230 with the conductive filler240, and an electrical path for the Vss is improved.

Via the wafer-bonding structure, it is favorable for improving theconductivity between the wafers and between the first metal layers andthe metal layers. Further, it is favorable for providing a more robustmechanical protection to avoid the edge chipping and the moisturepenetration during the sawing process. Also, it is favorable forimproving a reliability and a bouncing noise in device operation.

The foregoing description, for purpose of explanation, has beendescribed with reference to specific embodiments. It is to be noted thatTables show different data of the different embodiments; however, thedata of the different embodiments are obtained from experiments. Theembodiments were chosen and described in order to best explain theprinciples of the disclosure and its practical applications, to therebyenable others skilled in the art to best utilize the disclosure andvarious embodiments with various modifications as are suited to theparticular use contemplated. The embodiments depicted above and theappended drawings are exemplary and are not intended to be exhaustive orto limit the scope of the present disclosure to the precise formsdisclosed. Many modifications and variations are possible in view of theabove teachings.

1. A method of forming a wafer-bonding structure, comprising: awafer-bonding step, wherein at least two wafers are corresponding to andbonded to each other by bonding surfaces thereof; a through silicon via(TSV) forming step, wherein a TSV structure is formed on at least oneside of a seal ring structure of one of the at least two wafers, aconductive filler is disposed in the TSV structure, and the TSVstructure is overlapped the at least one side of the seal ring structureof one of the at least two wafers and a portion of a seal ring structureof another one of the at least two wafers; and a forming bonding padstep, wherein a bonding pad is formed on an outer surface which isrelative to the bonding surface of the wafer with the TSV structure, soas to form the wafer-bonding structure.
 2. The method of forming thewafer-bonding structure of claim 1, further comprising: a surfacetreatment step, wherein the bonding surface of each of the at least twowafers is performed a surface treatment before the wafer-bonding step.3. The method of forming the wafer-bonding structure of claim 1, whereinthe at least two wafers are exposed to a nitrogen plasma or an oxygenplasma in the wafer-bonding step.
 4. The method of forming thewafer-bonding structure of claim 1, wherein the at least two wafers arebonded at 250° C. to 350° C. for 1 hour to 3 hours in the wafer-bondingstep.
 5. The method of forming the wafer-bonding structure of claim 1,wherein the at least two seal ring structures are aligned to each otherin the wafer-bonding step.
 6. The method of forming the wafer-bondingstructure of claim 5, wherein an alignment accuracy of the wafer-bondingstep is below 300 nm.
 7. A wafer-bonding structure, comprising: at leasttwo wafers, which are bonded to each other, each of the at least twowafers having a bonding surface, and each of the at least two waferscomprising: a seal ring structure, disposed in the wafer, an end of theseal ring structure connected to the bonding surface, and the other endof the seal ring structure connected to an outer surface of the wafer; athrough silicon via (TSV) structure, passed through from the outersurface to the bonding surface in one of the at least two wafers,wherein the TSV structure is connected to and overlapped at least oneside of the seal ring structure of one of the at least two wafers and aportion of the seal ring structure of another one of the at least twowafers; a conductive filler, disposed in the TSV structure; and abonding pad, disposed on the outer surface of the wafer with the TSVstructure.
 8. The wafer-bonding structure of claim 7, wherein each ofthe seal ring structures comprises: a first metal layer, connected tothe bonding surface; at least one metal layer, disposed between theouter surface and the first metal layer; and at least two pin sets, oneof the least two pin sets connected to the first metal layer and the atleast one metal layer, the other one of the at least two pin setsconnected to the at least one metal layer and the outer surface, whereineach of the at least two pin sets comprises at least three pins.
 9. Thewafer-bonding structure of claim 8, wherein a range of the TSV structurestraddled the first metal layer is larger than or equal to 0.05 μm. 10.The wafer-bonding structure of claim 8, wherein a range of the TSVstructure straddled the at least one metal layer is larger than or equalto 0.02 μm.
 11. The wafer-bonding structure of claim 8, wherein a widthof each of the at least three pins is larger than or equal to 0.025 μm.12. The wafer-bonding structure of claim 8, wherein the first metallayer and the at least one metal layer are made of copper.
 13. Thewafer-bonding structure of claim 8, wherein a width of the first metallayer is larger than a width of the at least one metal layer.
 14. Thewafer-bonding structure of claim 7, wherein a depth of the TSV structureis 2 μm to 20 μm.
 15. The wafer-bonding structure of claim 7, wherein awidth of the TSV structure is 0.1 μm to 10 μm.
 16. The wafer-bondingstructure of claim 7, wherein the conductive filler is made of copper.17. The wafer-bonding assembly of claim 7, wherein the bonding pad ismade of aluminum.